Due to the decomposition temperature of Polyamide 66 (PA66) in the environment is close to its thermoforming temperature, it is difficult to construct porous scaffolds of PA66/nanohydroxyapatite (PA66/HAp) by fused deposition modeling (FDM) three-dimensional (3D) printing. In this study, we demonstrated for the first time a method for 3D printing PA66/HAp composites at room temperature, prepared PA66/HAp printing ink using a mixed solvent of formic acid/dichloromethane (FA/DCM), and constructed a series of composite scaffolds with varying HAp content. This printing system can print composite materials with a high HAp content of 60 wt %, which is close to the mineral content in natural bone. The physicochemical evaluation presented that the hydroxyapatite was uniformly distributed within the PA66 matrix, and the PA66/HAp composite scaffold with 30 wt % HAp content exhibited optimal mechanical properties and printability. The results of in vitro cell culture experiments indicated that the incorporation of HAp into the PA66 matrix significantly improved the cell adhesion, proliferation, and osteogenic differentiation of bone marrow stromal cells (BMSCs) cultured on the scaffold. In vivo animal experiments suggested that the PA66/HAp composite material with 30 wt % HAp content had the best structural maintenance and osteogenic performance. The three-dimensional PA66/HAp composite scaffold prepared by low temperature printing in the current study holds great potential for the repair of large-area bone defects.
Keywords: 3D print; bone regeneration; nanohydroxyapatite; polyamide 66.