The performance consistency of the gas sensor is strongly dependent on the interface binding between the sensitive materials and the electrodes. Traditional powder coating methods can inevitably lead to differences in terms of substrate-film interface interaction and device performance, affecting the stability and lifetime. Thus, efficient growth of sensitive materials on device substrates is crucial and essential to enhance the sensing performance, especially for stability. Herein, hierarchically ordered macro/mesoporous WO3 films are in situ synthesized on the electrode via a facile soft/hard dual-template strategy. Orderly arrayed uniform polystyrene (PS) microspheres with tailored size (ca. 1.2 µm) are used as a hard template, and surfactant Pluronic F127 as a soft template can co-assemble with tungsten precursor into ordered mesostructure in the interstitials of PS colloidal crystal induced by solvent evaporation. Benefiting from its rich porosity and high stability, the macro/mesoporous WO3-based sensor shows high sensitivity (Rair/Rgas = 307), fast response/recovery speed (5/9 s), and excellent selectivity (SH2S/Smax > 7) toward 50 ppm H2S gas (a biomarker for halitosis). Significantly, the sensors exhibit an extended service life with a negligible change in sensing performance within 60 days. This lab-on-device synthesis provides a platform method for constructing stable nanodevices with good consistency and high stability, which are highly desired for developing high-performance sensors.
Keywords: gas sensor; hierarchically porous structure; hydrogen sulfide; lab‐on‐device synthesis; tungsten oxides.
© 2024 Wiley‐VCH GmbH.