Among thermoelectric materials, skutterudites are the most prominent candidates in the mid-temperature range applications. In the multiple-filled Sr0.2Yb0.2Co4Sb12 skutterudite, with Sr and Yb as fillers, we have enhanced the thermoelectric performance of CoSb3 through the reduction of lattice thermal conductivity and the optimization of carrier concentration and electrical conductivity. The high-pressure synthesis of the double-filled derivative promotes filling fraction fluctuation. This is observed by high angular resolution synchrotron X-ray diffraction, showing a phase segregation that corresponds to an inhomogeneous distribution of the filler atoms, located at the 2a positions of the cubic space group Im3̅. In addition, scanning transmission electron microscopy (STEM) combined with EELS spectroscopy clearly shows a segregation of Sr atoms from the surface of the grains, which is compatible with the synchrotron X-ray powder diffraction results. Mean square displacement parameters analysis results in Einstein temperatures of ∼94 and ∼67 K for Sr and Yb, respectively, and a Debye temperature of ∼250 K. The strong effect on resonant and disorder scattering yields a significantly lower lattice thermal conductivity of 2.5 W m-1 K-1 at 773 K. Still, good weighed-mobility values were obtained, with high filling fraction of the Yb and Sr elements. This drives a reduced electrical resistivity of 2.1 × 10-5 Ω m, which leads to a peak zT of 0.26 at 773 K. The analysis and results performed for the synthesized (Sr,Yb)-double filled CoSb3, shed light on skutterudites for potential waste-heat recovery applications.
© 2024 The Authors. Published by American Chemical Society.