The improper disposal of plastics is a growing concern due to increasing global environmental problems such as the rise of CO2 emissions, diminishing petroleum sources, and pollution, which necessitates the research and development of biodegradable materials as an alternative to conventional packaging materials. The purpose of this research was to analyse the properties of biodegradable polymer blends of thermoplastic potato starch (TPS) and polylactide, (PLA) without and with the addition of citric acid (CA) as a potential compatibilizer and plasticizer. The prepared blends were subjected to a comprehensive physicochemical characterization, which included: FTIR-ATR spectroscopy, morphological analysis by scanning electron microscopy (SEM), determination of thermal and mechanical properties by differential scanning calorimetry (DSC), water vapour permeability (WVP), as well as biodegradation testing in soil. The obtained results indicate an improvement in adhesion between the TPS and PLA phases due to the addition of citric acid, better homogeneity of the structure, and greater compatibility of the polymer blends, leading to better thermal, mechanical and barrier properties of the studied biodegradable TPS/PLA polymer blends. After conducting the comprehensive research outlined in this paper, it has been determined that the addition of 5 wt.% of citric acid serves as an effective compatibilizer and plasticizer. This supplementation achieves an optimal equilibrium across thermal, mechanical, morphological, and barrier properties, while also promoting material sustainability through biodegradation. In conclusion, it can be stated that the use of thermoplastic starch in TPS/PLA blends accelerates the biodegradation of PLA as a slowly biodegradable polymer. While the addition of citric acid offers significant advantages for TPS/PLA blends, further research is needed to optimize the formulation and processing parameters to achieve the desired balance between mechanical strength, thermal and barrier properties and biodegradability.
Keywords: biodegradation; biomaterials; blends; citric acid; polylactic acid; potato starch.