Bio-based epoxy resins have received significant attention in terms of concerns regarding carbon emission. Epoxidized soybean oil (ESO) derived from sustainable feedstock has been widely used to blend with traditional diglycidyl ether of bisphenol-A (DGEBA) to replace some of the petroleum-based components. In this work, molecular dynamics (MD) simulations were applied to track the network formation and predict the performance of methyl hexahydrophthalic anhydride (MHHPA)-cured ESO/DGEBA blend systems. The effects of ESO content and cross-linking degree on the mass density, volumetric shrinkage, glass transition temperature (Tg), coefficient of thermal expansion (CTE), Young's modulus, yield strength, and Poisson's ratio of the epoxy resin were systematically investigated. The results show that systems with high ESO content achieve gelation at low cross-linking degree. The Tg value, Young's modulus, and yield strength increase with the increase in cross-linking degree, but the CTE at the glassy state and Poisson's ratio decrease. The comparison results between the simulated and experimental data demonstrated that the MD simulations can accurately predict the thermal and mechanical properties of ESO-based thermosets. This study gains insight into the variation in thermo-mechanical properties of anhydride-cured ESO/DGEBA-based epoxy resins during the cross-linking process and provides a rational strategy for optimizing bio-based epoxy resins.
Keywords: MD simulation; bio-based thermoset; cross-linking.