This study aimed to evaluate the dimensional stability of maxillary diagnostic casts fabricated from a biobased model resin, which consists of 50% renewable raw materials for sustainable production, a model resin, and stone, over one month. A master maxillary stone cast was digitized with a laboratory scanner to generate a reference file. This master cast was also scanned with an intraoral scanner to additively manufacture casts with a biobased model resin (BAM) and a model resin (AM). Polyvinylsiloxane impressions of the master cast were also made and poured in type III stone (CV) (n = 8). The same laboratory scanner was used to digitize each model one day (T0), 1 week (T1), 2 weeks (T2), 3 weeks (T3), and 4 weeks (T4) after fabrication. Deviations from the reference file were calculated with an analysis software and analyzed with generalized linear model analysis (α = 0.05). The interaction between the material and the time point affected measured deviations (p < 0.001). Regardless of the time point, CV had the lowest and AM had the highest deviations (p < 0.001). BAM mostly had lower deviations at T0 and mostly had higher deviations at T4 (p ≤ 0.011). AM had the highest deviations at T4 and then at T3, whereas it had the lowest deviations at T0 (p ≤ 0.002). The measured deviations of CV increased after each time point (p < 0.001). BAM casts had deviations within the previously reported clinically acceptable thresholds over one month and had acceptable dimensional stability. Therefore, tested biobased resin may be a viable alternative for the sustainable manufacturing of maxillary diagnostic casts that are to be used clinically.
Keywords: additive manufacturing; biobased model resin; dental cast; dimensional stability; sustainable manufacturing.