A promising method for additive manufacturing that makes it possible to produce intricate and personalized parts is selective laser melting (SLM). However, the mechanical properties of as-corroded SLM parts are still areas of concern. This research investigates the mechanical behavior of SLM parts that are exposed to a saline environment containing a 3.5% NaCl solution for varying lengths of time. The exposure times chosen for this study were 10 days, 20 days, and 30 days. The results reveal that the tensile strength of the parts is significantly affected by the duration of exposure. Additionally, the study also examined the influence of porosity on the corrosion behavior of the parts. The analysis included studying the mass loss of the parts over time, and a regression analysis was conducted to analyze the relationship between exposure time and mass loss. In addition, the utilization of scanning electron microscopy (SEM) and X-ray photo spectroscopy (XPS) techniques yielded valuable insights into the fundamental mechanisms accountable for the observed corrosion and mechanical behavior. It was found that the presence of corrosion products (i.e., oxide layer) and pitting contributed to the degradation of the SLM parts in the saline environment. This research emphasizes the importance of considering part thickness in the design of SLM components for corrosive environments and provides insights for enhancing their performance and durability.
Keywords: AlSi10Mg; NaCl solution; corrosion behavior; exposure time; mass loss; mechanical properties; selective laser melting (SLM).