This study investigates the origin of low-pressure hysteresis (LPH) in the adsorption and desorption of three different probe molecules: carbon dioxide, nitrogen, and argon, across various adsorption temperatures (from cryogenic to room temperature), and within five different carbon materials: synthetic carbons (pristine and one post-synthetically oxidized) and natural coal. Significant attention is dedicated to elucidating LPH in oxidized samples outgassed at various temperatures (120-350 °C). Experimental results show that insufficient outgassing temperature can lead to unreliable data due to artificial LPH and significantly underestimated textural properties, primarily caused by porosity blockage from substances like moisture. Conversely, in samples where heteroatoms have a stabilizing effect on texture, such as natural coal, careful consideration of outgassing temperature is crucial due to the risk of thermal degradation. Other factors contributing to LPH are adsorption temperature, and especially, kinetic limitations at cryogenic temperatures for cellulose-based carbons. Minor factors responsible for LPH are the physical state of the sample (monolith vs powder) and the flexibility of the porous system, both studied by carbon dioxide sorption. This study constitutes an important piece in the evaluation of LPH, providing practical recommendations and underlining the importance of experimental design, with implications for further research in this complex field.
Keywords: artificial hysteresis; degassing; diffusion limitations; open isotherms; oxidized carbon.
© 2024 The Authors. Small published by Wiley‐VCH GmbH.