Stability and photocurrent enhancement of photodetectors by using core/shell structured CsPbBr3/TiO2 quantum dots and 2D materials

Chathurika Maduwanthi; Chao-An Jong; Waleed S Mohammed; Shu-Han Hsu

doi:10.1039/d3na01129a

Stability and photocurrent enhancement of photodetectors by using core/shell structured CsPbBr₃/TiO₂ quantum dots and 2D materials

Nanoscale Adv. 2024 Apr 2;6(9):2328-2336. doi: 10.1039/d3na01129a. eCollection 2024 Apr 30.

Authors

Chathurika Maduwanthi¹, Chao-An Jong², Waleed S Mohammed³, Shu-Han Hsu¹

Affiliations

¹ School of Integrated Science and Innovation, Sirindhorn International Institute of Technology, Thammasat University Pathum Thani 12120 Thailand shuhanhsu@siit.tu.ac.th.
² Taiwan Semiconductor Research Institute, National Applied Research Laboratories Hsinchu 300091 Taiwan ROC.
³ Center of Research in Optoelectronics, Communication and Control Systems (BU-CROCCS), Bangkok University Pathum Thani 12120 Thailand.

Abstract

Ultra-stable CsPbBr₃ perovskite quantum dots (QDs) were prepared, and the performance of the photodetector fabricated from them was enhanced by 2D material incorporation. This multi-component photodetector appears to have good stability in the ambient utilization environment. All inorganic CsPbBr₃ QDs are potential candidates for application in photodetection devices. However, QDs have several issues such as defects on the QD surface, degradation under environmental conditions, and unfavorable carrier mobility limiting the high performance of the photodetectors. This work addresses these issues by fabricating a core/shell structure and introducing 2D materials (MXenes, Ti₃C₂T_x) into the device. Here, three types of photodetectors with QDs only, QDs with a core/shell structure, and QDs with a core/shell structure and MXenes are fabricated for systematic study. The CsPbBr₃/TiO₂ photodetector demonstrated a two times photocurrent enhancement compared to bare QDs and had good device stability after TiO₂ shell coating. After introducing Ti₃C₂T_x into CsPbBr₃/TiO₂, a significant photocurrent enhancement from nanoampere (nA) to microampere (μA) was observed, revealing that MXenes can improve the photoelectric response of perovskite materials significantly. Higher photocurrent can avoid signal interference from environmental noise for better practical feasibility. This study provides a systematic understanding of the photocurrent conversion of perovskite quantum dots that is beneficial in advancing optoelectronic device integration, especially for flexible wearable device applications.