Purpose: To investigate the in vitro biocompatibility of human gingival fibroblasts with preformed paediatric crowns and resistance to acid exposure at levels that simulate the oral environment.
Methods: This laboratory study investigated primary HGFs viability, metabolic activity, cytotoxicity, and apoptotic events on preformed metal crown discs, composite resin-coated wells, and monolithic zirconia fragments at 24, 48, and 72 h using the ApoTox-Glo Triplex assay. The PPCs were also immersed in 0.1% lactic acid, 0.2% phosphoric acid, or 10% citric acid for 7 days at 37 °C to reproduce conditions associated with dietary intake or gastric reflux. Samples were then subject to inductively coupled plasma optical emission spectrometry to quantitate the release of ions.
Results: The viability of HGFs on stainless steel and CR significantly declined at 48 and 72 h, representing potential cytotoxicity (p < 0.05). Cytotoxicity of HGFs was also higher for stainless steel and ZR compared to control (p < 0.05). PMCs and ZR crowns gave minimal ion release. Meanwhile, significant quantities of metallic ions, including copper (Cu), iron (Fe), nickel (Ni), and zinc (Zn), were present in eluates from veneered-preformed metal crowns.
Conclusion: As PPCs can be exposed to highly acidic environments for many years, thus the release of metallic ions from V-PMCs should form the further investigation in future studies.
Keywords: Acidity; Biocompatibility; Gingival fibroblasts; Ion release; Preformed paediatric crowns.