Coatings prepared from chromia-rich (Al,Cr)2O3 solid solution (ss) feedstock powders are intended to improve the properties of Cr2O3 coatings, but are rarely studied so far. In this work, the processability of a commercial (Al,Cr)2O3 solid solution (ss) powder containing 78 wt.% Cr2O3 by atmospheric plasma spraying (APS), the corresponding coating microstructures and properties were investigated. Possible further improvements were expected by blending with 2, 23 and 54 wt.% TiOx powder. For comparison, plain Cr2O3 and TiOx coatings were studied as well. The microstructures were analyzed using SEM, EDS and XRD measurements. Hardness (HV0.3) was measured, as well as the dry unidirectional sliding wear resistance and the abrasion wear resistance (ASTM G65). Moreover, the corrosion and electrical insulating properties were measured. The (Al,Cr)2O3 ss showed only a small change of the composition, and the formation of γ-Al2O3, as found for alumina-rich (Al,Cr)2O3 ss powders, was avoided. Compared to the plain chromia coating, some improvements of the processability and coating properties for the ss (Al,Cr)2O3 coating were found. The most balanced coating performance was achieved by blending the ss (Al,Cr)2O3 with 2 wt.% TiOx, as this coating showed both a high sliding and abrasion wear resistance, in combination with a high corrosion resistance.
Keywords: alumina; atmospheric plasma spray (APS); ceramic coating; chromia; properties; ternary system; titania.
© The Author(s) 2021.