The microstructures and mechanical properties of equiatomic CoCrFeMnNi high-entropy alloys (HEAs) treated with various processing parameters of laser surface heat treatment are studied in this paper. The typical inverse gradient-grained structure, which is composed of a hard central layer and a soft surface layer, can be obtained by laser surface heat treatment. A much narrower gradient layer leads to the highest yield strength by sacrificing ductility when the surface temperature of the laser-irradiated region remains at ~850 °C, whereas the fully recrystallized microstructure, which exists from the top surface layer to the ~1.05 mm depth layer, increases the ductility but decreases the yield strength as the maximum heating temperature rises to ~1050 °C. Significantly, the superior strength-ductility combination can be acquired by controlling the surface temperature of a laser-irradiated surface at ~1000 °C with a scanning speed of ~4 mm/s due to the effect of hetero-deformation-induced strengthening and hardening, as well as the enhanced interaction between dislocation and nanotwins by the hierarchical nanotwins. Therefore, retaining the partial recrystallized microstructure with a relatively high microhardness in the central layer, promoting the generation of hierarchical nanotwins, and increasing the volume proportion of gradient layer can effectively facilitate the inverse gradient-grained CoCrFeMnNi HEAs to exhibit a desirable strength-ductility synergy.
Keywords: hierarchical nanotwins; high-entropy alloy; inverse gradient-grained structure; laser surface heat treatment; strength–ductility synergy.