Fe-~30 at.%Pd is a ferromagnetic shape memory alloy (SMA) with a reversible thermoelastic fcc-fct phase transformation. The advantage of adding a small amount of Indium to Fe-Pd SMAs is, among other things, the upward shift of the transformation temperatures, which allows us to maintain the material in the martensitic state (fct structure) at room temperature. In this work, we study the microstructure and the magnetic properties of nominally Fe67.6-Pd32-In0.4 (at.%) melt-spun ribbons. Energy-dispersive spectroscopy analysis showed a certain level of non-uniformity of Indium distribution in the as-spun ribbon. However, the attempt to homogenize the ribbon by annealing at 1273 K for 120 h resulted in an unfavoured structural change to bct martensite. Magneto strains induced by a 9 kOe magnetic field reached over 400 ppm for certain field orientations, which is around four times more than the magneto strains of near-binary Fe-Pd shape memory alloys.
Keywords: Fe-Pd shape memory alloy; X-ray diffraction; magnetically induced strains; martensitic transformation; multiferroic alloys.