Detailed analyses of the reasons for changes in the mechanical parameters of fiberglass exposed to different climatic zones have been made available in the literature; however, such detailed studies of basalt plastic do not yet exist. It is possible to make reasonable conclusions on the climatic resistance of reinforced plastics by monitoring the deformation-strength characteristics in combination with fractographic and DMA analyses of the solar- and shadow-exposed parts of the plastics; additionally, one can conduct analyses of the IR spectrum and the moisture sorbtion kinetics. As a starting point for the climatic aging of polymer composite materials, it is necessary to accept the time of exposure in which the maximum values of the elastic strength properties of polymeric materials are achieved. Based on the results of the DMA analysis, it was found that, unlike basalt-reinforced plastics (where the material is post-cured exclusively at the initial stage of the exposure), in glass-reinforced plastic, a process of destruction occurs. The formation of internal stresses in the material and their growth were determined through observing the duration of climatic exposure. The formation of closed porosity, depending on the duration of exposure, can be assessed using the values of the increase in the average moisture content. A set of experimental studies has established that glass-reinforced plastics are subject to greater destruction under the influence of a very cold climate than the basalt-reinforced plastic.
Keywords: basalt-reinforced plastic; climatic resistance; deformation–strength characteristics; glass-reinforced plastic.