Decoration of Carbon Dots on Oxygen-Vacancy-Enriched S-Scheme TiO2 Quantum Dots/TiO2 Oxygen Vacancies Photocatalysts: Impressive Quantum-Dot-Sized Photocatalysts for Remediation of Antibiotics, Bacteria, and Dyes

Aziz Habibi-Yangjeh; Khadijeh Pournemati; Ziba Ahmadi; Alireza Khataee

doi:10.1021/acs.langmuir.4c00060

Decoration of Carbon Dots on Oxygen-Vacancy-Enriched S-Scheme TiO₂ Quantum Dots/TiO₂ Oxygen Vacancies Photocatalysts: Impressive Quantum-Dot-Sized Photocatalysts for Remediation of Antibiotics, Bacteria, and Dyes

Langmuir. 2024 Apr 23;40(16):8503-8519. doi: 10.1021/acs.langmuir.4c00060. Epub 2024 Apr 12.

Authors

Aziz Habibi-Yangjeh¹, Khadijeh Pournemati¹, Ziba Ahmadi², Alireza Khataee^{3

4}

Affiliations

¹ Department of Chemistry, Faculty of Science, University of Mohaghegh Ardabili, 56199-13131 Ardabil, Iran.
² Department of Biology, Faculty of Science, University of Mohaghegh Ardabili, 56199-13131 Ardabil, Iran.
³ Research Laboratory of Advanced Water and Wastewater Treatment Processes, Department of Applied Chemistry, Faculty of Chemistry, University of Tabriz, 51666-16471 Tabriz, Iran.
⁴ Department of Chemical Engineering, Istanbul Technical University, 34469 Istanbul, Turkey.

PMID: 38608275
DOI: 10.1021/acs.langmuir.4c00060

Abstract

Today, cleaning the environment using photocatalytic technology is one of the main research activities. In this study, carbon dots (C-dots) were anchored on oxygen-vacancy-enriched TiO₂ quantum dots (QDs)/TiO₂ oxygen vacancies (OVs) using a facile procedure. The resultant ternary TiO₂ QDs/TiO₂ OVs/C-dots photocatalysts with a quantum dot size of almost 4.55 nm were used for detoxification of aqueous solutions containing four antibiotics and three organic dyes as well as inactivation of two pathogenic bacteria, including Escherichia coli and Staphylococcus aureus, upon visible light. The degradation constant of tetracycline over the optimized TiO₂ QDs/TiO₂ OVs/C-dots nanocomposite reached 714 × 10^-4 min^-1, which was 17.3, 12.1, and 2.92 times higher than TiO₂ QDs, TiO₂ OVs, and TQDs/TOVs (1:1) materials, respectively. Effective separation of electron-hole pairs between TiO₂ QDs and TiO₂ OVs counterparts through decorated C-dots by an established S-scheme system was the main reason for boosted photocatalytic activity. With regard to the facile growth of wheat and lentil seeds in the treated solutions, it is hoped that the TiO₂ QDs/TiO₂ OVs/C-dots nanocomposite with significant stability could be used to clean up wastewaters.