Polyamide 11 (PA11) and copolyester (TPC-E) were compounded through melt extrusion with low levels (below 10%) of expanded graphite (EG), aiming at the manufacturing of a thermally and electrically conductive composite resistant to friction and with acceptable mechanical properties. Thermal characterisation showed that the EG presence had no influence on the onset degradation temperature or melting temperature. While the specific density of the produced composite materials increased linearly with increasing levels of EG, the tensile modulus and flexural modulus showed a significant increase already at the introduction of 1 wt% EG. However, the elongation at break decreased significantly for higher loadings, which is typical for composite materials. We observed the increase in the dielectric and thermal conductivity, and the dissipated power displayed a much larger increase where high frequencies (e.g., 10 GHz) were taken into account. The tribological results showed significant changes at 4 wt% for the PA11 composite and 6 wt% for the TPC-E composite. Morphological analysis of the wear surfaces indicated that the main wear mechanism changed from abrasive wear to adhesive wear, which contributes to the enhanced wear resistance of the developed materials. Overall, we manufactured new composite materials with enhanced dielectric properties and superior wear resistance while maintaining good processability, specifically upon using 4-6 wt% of EG.
Keywords: dielectric properties; expanded graphite; material characterisation; polymer composites; tribology.