In this study, thiol-functionalized ladder-like polysesquioxanes end-capped with methyl and phenyl groups were synthesized via a simple sol-gel method and characterized through gel permeation chromatography (GPC), Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance (NMR), and thermogravimetric analysis (TGA). Additionally, epoxy blends of different formulations were prepared. Their structural, flame-retardant, thermal, and mechanical properties, as well as volatile organic compound (VOC) emissions, were determined using differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), TGA, scanning electron microscopy (SEM), limiting oxygen index (LOI), cone calorimetry, and a VOC analyzer. Compared to epoxy blends with flame retardants containing elemental phosphorus alone, those with flame retardants containing elemental phosphorus combined with silicon and sulfur exhibited superior thermal, flame-retardant, and mechanical properties with low VOC emissions. SEM of the residual char revealed a dense and continuous morphology without holes or cracks. In particular, LOI values for the combustion of methyl and phenyl end-capped polysilsesquioxane mixtures were 32.3 and 33.7, respectively, compared to 28.4% of the LOI value for the blends containing only phosphorus compounds. The silicon-sulfur-phosphorus-containing blends displayed reduced flammability concerning the blends using a flame retardant containing only phosphorus. This reflects the cooperative effects of various flame-retardant moieties.
Keywords: cooperative effects; epoxy resin; flame retardant; polysilsesquioxane; residual char.