High-temperature (HT) geothermal wells can provide green power 24 hours a day, 7 days a week. Under harsh environmental and operational conditions, the long-term durability requirements of such wells require special cementitious composites for well construction. This paper reports a comprehensive assessment of geothermal cement composites in cyclic pressure function laboratory tests and field exposures in an HT geothermal well (300-350 °C), as well as a numerical model to complement the experimental results. Performances of calcium-aluminate cement (CAC)-based composites and calcium-free cement were compared against the reference ordinary Portland cement (OPC)/silica blend. The stability and degradation of the tested materials were characterized by crystalline composition, thermo-gravimetric and elemental analyses, morphological studies, water-fillable porosity, and mechanical property measurements. All CAC-based formulations outperformed the reference blend both in the function and exposure tests. The reference OPC/silica lost its mechanical properties during the 9-month well exposure through extensive HT carbonation, while the properties of the CAC-based blends improved over that period. The Modified Cam-Clay (MCC) plasticity parameters of several HT cement formulations were extracted from triaxial and Brazilian tests and verified against the experimental results of function cyclic tests. These parameters can be used in well integrity models to predict the field-scale behavior of the cement sheath under geothermal well conditions.
Keywords: calcium-free well cement; calcium–aluminate well cement; finite element modeling; function cement tests; geothermal cement; high-temperature OPC; high-temperature cement CO2 resistance.