Gel polymer electrolytes (GPEs) have high safety and excellent electrochemical performance, so applying GPEs in lithium batteries has received much attention. However, their poor lithium ion transfer number, cycling stability, and low room temperature ionic conductivity seriously affect the utilization of gel polymer electrolytes. This paper successfully synthesized flexible poly (vinylidene fluoride-hexafluoropropylene)-lithium titanium aluminum phosphate (PVDF-HFP-LATP) gel polymer electrolytes using the immersion precipitation method. The resulting GPE has a porous honeycomb structure, which ensures that the GPE has sufficient space to store the liquid electrolyte. The GPE has a high ionic conductivity of 1.03 ×10-3 S cm-1 at room temperature (25 °C). The GPE was applied to LiFePO4/GPE/Li batteries with good rate performance at room temperature. The discharge specific capacity of 1C was as high as 121.5 mAh/g, and the capacity retention rate was 94.0% after 300 cycles. These results indicate that PVDF-HFP-LATP-based GPEs have the advantage of simplifying the production process and can improve the utility of gel polymer lithium metal batteries.
Keywords: LATP; excellent rate performance; gel polymer electrolytes; the immersion precipitation method.