Solubilization and structural changes of lignin in naked oat stems during subcritical water autohydrolysis

Abstract

In this study, the solubilization and structural changes of lignin in naked oat stems were investigated under subcritical water autohydrolysis systems (170-210 °C, 0.68-1.85 MPa). In this system, Hemicellulose was preferentially hydrolyzed in the liquid water at elevated temperatures, leading to the production of acetic acid and glucuronic acid, which acidified the reaction system. Under acidic and high-temperature conditions, lignin primarily underwent degradation and condensation reactions. At autohydrolysis temperatures below 190 °C and autohydrolysis pressures below 1.22 MPa, lignin degradation was predominant, realizing a maximum lignin removal of 47.8 % and breakage of numerous β-O-4 bonds from lignin. At autohydrolysis temperatures above 190 °C and autohydrolysis pressures above 1.22 MPa, lignin condensation dominated, with an increase in the amount of organic acids generated upon hemicellulose degradation, leading to condensation reactions with the degraded low-molecular-weight lignin. The degree of lignin condensation was positively correlated with the temperature of the reaction system. This study provides essential insights into the dynamic changes in the structure of lignin in both the hydrolysis residue and hydrolysis solution during subcritical water autohydrolysis.

Keywords: Autohydrolysis; Lignin structural change; Reaction mechanism.