Hot compression tests were conducted to explore the deformation behavior of an extruded 7075 aluminum alloy bar at elevated temperatures. Specimens with 0°, 45°, and 90° angles along the extrusion direction were prepared. The compression temperatures were 300 and 400 °C, and the strain rates ranged from 0.001 to 0.1 s-1. The corresponding microstructures were characterized via OM and TEM, and the macroscopic texture was tested using XRD. The results indicated that the strength of the 7075 alloy decreases with higher compression temperatures and is in a proportional relationship with respect to the strain rate. During high-temperature compression, it is easier to stimulate atomic diffusion in the matrix, which can improve thermal activation abilities and facilitate dynamic recovery and dynamic recrystallization. In addition, the coarsening of precipitates also contributed to dynamic softening. When compressed at 300 °C, the stress levels of the 0° specimens ranked first, and those for the 45° specimens were the lowest. When compressed at 400 °C, the flow stresses of the specimens along three directions were comparable. The anisotropic mechanical behavior can be explained by the fiber grains and brass {011} <211> texture component. However, higher temperature deformation leads to recrystallization, which can weaken the anisotropy of mechanical properties.
Keywords: 7075 alloy; hot deformation; mechanical properties; microstructure; texture.