Two new congruently melting Pb-containing halogen silicates, Pb3[O10Pb20](SiO4)4X10 (X = Cl, Br), have been synthesized using a high-temperature solution method. Their crystal structures were determined by single-crystal X-ray diffraction, and both compounds crystallize in the orthorhombic space group Cmca. In both structures, the mirror-symmetric bilayer composed of Pb-O polyhedra is observed for the first time in Pb-containing silicates and belongs to α-PbO derivatives and is related to the Aurivillius phase. Thermal behavior analysis, UV-vis diffuse-reflectance spectroscopy, and IR spectroscopy were also performed. The Pb3[O10Pb20](SiO4)4Cl10 matrix was doped with Eu3+ ions as a dopant, and its potential application in fluorescence was confirmed from the resulting orange-red emission.