Although most semiconductor metal oxides including In2O3 show acceptable sensitivity to volatile organic compounds, it is difficult to detect ethanol effectively at low operating temperatures and detection levels. In this study, pure and Co-, Ni-, and Cu-doped In2O3 products with their doping content maintained at 1 mol % were successfully produced using a hydrothermal approach. Explicit contrast on the structural, microstructural, and textural properties of the synthesized In2O3 products was examined to determine their gas sensing performance. The Cu-doped In2O3 sensor demonstrated improved response of 15.3 to 50 ppm ethanol and has satisfactory selectivity, stability, low detection limit of 0.2, humidity resistance, and decreased working temperature of 80 °C compared to 150 °C of the pure In2O3 sensor. This optimal gas sensing performance is derived from the cube-like morphology assembled with interlinked nanoparticles, which favors trapping more target gas molecules and exposing more active sites, thereby greatly improving its sensing ability. This study showed that the Cu-doped In2O3 sensor with 1 mol % is suitable for monitoring ethanol gas for food safety applications.
© 2024 The Authors. Published by American Chemical Society.