All-Covalent Organic Framework Nanofilms Assembled Lithium-Ion Capacitor to Solve the Imbalanced Charge Storage Kinetics

Xiaoyang Xu; Jia Zhang; Zihao Zhang; Guandan Lu; Wei Cao; Ning Wang; Yunmeng Xia; Qingliang Feng; Shanlin Qiao

doi:10.1007/s40820-024-01343-2

All-Covalent Organic Framework Nanofilms Assembled Lithium-Ion Capacitor to Solve the Imbalanced Charge Storage Kinetics

Nanomicro Lett. 2024 Feb 15;16(1):116. doi: 10.1007/s40820-024-01343-2.

Authors

Xiaoyang Xu^#¹, Jia Zhang^#^{1

2}, Zihao Zhang¹, Guandan Lu¹, Wei Cao¹, Ning Wang², Yunmeng Xia^{1

2}, Qingliang Feng³, Shanlin Qiao^{4

5}

Affiliations

¹ College of Chemistry and Pharmaceutical Engineering, Hebei University of Science and Technology, Shijiazhuang, 050018, People's Republic of China.
² School of Chemistry and Chemical Engineering, Northwestern Polytechnical University, Xi'an, 710072, People's Republic of China.
³ School of Chemistry and Chemical Engineering, Northwestern Polytechnical University, Xi'an, 710072, People's Republic of China. fengql@nwpu.edu.cn.
⁴ College of Chemistry and Pharmaceutical Engineering, Hebei University of Science and Technology, Shijiazhuang, 050018, People's Republic of China. ccpeslqiao@hebust.edu.cn.
⁵ Hebei Engineering Research Center of Organic Solid Photoelectric Materials for Electronic Information, Shijiazhuang, 050018, People's Republic of China. ccpeslqiao@hebust.edu.cn.

^# Contributed equally.

Abstract

Free-standing covalent organic framework (COFs) nanofilms exhibit a remarkable ability to rapidly intercalate/de-intercalate Li⁺ in lithium-ion batteries, while simultaneously exposing affluent active sites in supercapacitors. The development of these nanofilms offers a promising solution to address the persistent challenge of imbalanced charge storage kinetics between battery-type anode and capacitor-type cathode in lithium-ion capacitors (LICs). Herein, for the first time, custom-made COF_BTMB-TP and COF_TAPB-BPY nanofilms are synthesized as the anode and cathode, respectively, for an all-COF nanofilm-structured LIC. The COF_BTMB-TP nanofilm with strong electronegative-CF₃ groups enables tuning the partial electron cloud density for Li⁺ migration to ensure the rapid anode kinetic process. The thickness-regulated cathodic COF_TAPB-BPY nanofilm can fit the anodic COF nanofilm in the capacity. Due to the aligned 1D channel, 2D aromatic skeleton and accessible active sites of COF nanofilms, the whole COF_TAPB-BPY//COF_BTMB-TP LIC demonstrates a high energy density of 318 mWh cm^-3 at a high-power density of 6 W cm^-3, excellent rate capability, good cycle stability with the capacity retention rate of 77% after 5000-cycle. The COF_TAPB-BPY//COF_BTMB-TP LIC represents a new benchmark for currently reported film-type LICs and even film-type supercapacitors. After being comprehensively explored via ex situ XPS, ⁷Li solid-state NMR analyses, and DFT calculation, it is found that the COF_BTMB-TP nanofilm facilitates the reversible conversion of semi-ionic to ionic C-F bonds during lithium storage. COF_BTMB-TP exhibits a strong interaction with Li⁺ due to the C-F, C=O, and C-N bonds, facilitating Li⁺ desolation and absorption from the electrolyte. This work addresses the challenge of imbalanced charge storage kinetics and capacity between the anode and cathode and also pave the way for future miniaturized and wearable LIC devices.

Keywords: Charge storage kinetic; Covalent organic frameworks; Lithium-ion capacitor.