Development of natural attapulgite derived ferromanganese spinel oxides as heterogeneous catalysts for persulfate activation of tetracycline degradation

Abstract

Ferromanganese spinel oxides (MnFe₂O₄, MFO) have been proven effective in activating persulfate for pollutants removal. However, their inherent high surface energy often leads to agglomeration, diminishing active sites and consequently restricting catalytic performance. In this study, using Al-MCM-41 (MCM) mesoporous molecular sieves derived from natural attapulgite as a support, the MFO/MCM composite was synthesized through dispersing MnFe₂O₄ nanoparticles on MCM carrier by a simple hydrothermal method, which can effectively activate persulfate (PS) to degrade Tetracycline (TC). The addition of Al-MCM-41 can effectively improve the specific surface area and adsorption performance of MnFe₂O₄, but also reduce the leaching amount of metal ions. The MFO/MCM composite exhibited superior catalytic reactivity towards PS and 84.3% removal efficiency and 64.7% mineralization efficiency of TC (20 mg/L) was achieved in 90 min under optimized conditions of 0.05 mg/L catalyst dosage, 5 mM PS concentration, room temperature and no adjustment of initial pH. The effects of various stoichiometric MFO/MCM ratio, catalyst dosage, PS concentration, initial pH value and co-existing ions on the catalytic performance were investigated in detail. Moreover, the possible reaction mechanism in MFO-MCM/PS system was proposed based on the results of quenching tests, electron paramagnetic resonance (EPR) and XPS analyses. Finally, major degradation intermediates of TC were detected by liquid chromatography mass spectrometry technologies (LC-MS) and four possible degradation pathways were proposed. This study enhances the design approach for developing highly efficient, environmentally friendly and low-cost catalysts for the advanced treatment process of antibiotic wastewater.

Keywords: Al-MCM-41; MnFe(2)O(4); Persulfate; Singlet oxygen; Tetracycline.