This study is focused on investigating the rheological and mechanical properties of highly oxidized graphite (GrO) incorporated into a poly (lactic acid) (PLA) matrix composite. Furthermore, the samples were annealed at 110 °C for 30 min to study whether GrO concentration has an effect on the elastic modulus (E') after treatment. The incorporation of GrO into PLA was carried out by employing an internal mixing chamber at 190 °C. Six formulations were prepared with GrO concentrations of 0, 0.1, 0.5, 1, 1.5, and 3 wt%. The thermal stability, thermomechanical behavior, and crystallinity of the composites were evaluated utilizing thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), and differential scanning calorimetry DSC, respectively. The thermal stability (according to Tmax) of the PLA/GrO composites did not change substantially compared with PLA. According to DSC, the crystallinity increased until the GrO concentration reached 1 wt% and afterward decreased. Regarding the heat treatment of the PLA/GrO composites, the E' increased (by two orders of magnitude) at 80 °C with the maximum value achieved at 1 wt% GrO compared with the non-heat-treated composites.
Keywords: PLA; crystallinity grade; expanded graphite; mechanical properties.