In this study, four different plastic materials usually used in the agricultural sector (polystyrene film (PS), polyethylene terephthalate film (PET), low-density polyethylene film (LDPE) and linear low-density polyethylene film (LLDPE)) were subjected to different abiotic treatments, including photo-oxidation (ultraviolet and e-beam radiation) and thermochemical treatments, to enhance polymer degradation. The extensive use of these polymers leads to large amounts of plastic waste generation, including small plastic pieces, known as microplastics, which affect the quality of the agricultural environment, including soil fertility and quality. Therefore, polymer degradation strategies are needed to effectively reduce plastic waste to protect the agricultural sector. The degree of polymer degradation was assessed by the use of thermal and spectroscopic analyses, such as TGA and FTIR. In addition, efficiency, cost-benefits, and potential side-effects were also evaluated to propose the optimal degradation strategy to reduce plastic waste from the point of view of efficiency. The results obtained showed that the pre-treatments based on photo-oxidation (ultraviolet B and C and e-beam radiation) were more efficient and had a better cost-benefit for the degradation of the polymers studied in relation to the thermochemical treatments. Specifically, ultraviolet photo-oxidation worked well for PS and PET, requiring low energy and medium times. However, e-beam radiation was recommended for PE (LDPE and LLDPE) degradation, since high energy and long times were needed when ultraviolet energy was applied to this polymer. Furthermore, the overall efficiency of the plastic degradation of pre-treatments should be studied using a multicriteria approach, since FTIR assessments, in some cases, only consider oxidation processes on the plastic surface and do not show the potential integrity changes on the plastic probes.
Keywords: FTIR; agri-food waste plastic; e-beam; linear low density of polyethylene; low density polyethylene; polyethylene terephthalate; polystyrene; thermal analyses.