α-Fe2O3 and FeMnO3/α-Fe2O3 fibers were successfully prepared via Solution Blow Spinning (SBS). The effect of drying during the SBS process on fiber morphology was evaluated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and N2 adsorption-desorption isotherms. A slow drying promoted continuous fibers with rough surfaces and lower average diameters. However, fast drying enabled the production of fibers with low densification and many surface pores with higher BET-specific surface areas. The porous fibers produced have potential applications in energy generation and storage.
Keywords: A-HSBS; FeMnO3/α-Fe2O3; fast drying; fibers.