Niobium pentoxides (Nb2O5) present great potential as next-generation anode candidates due to exceptional lithium-ion intercalation kinetics, considerably high capacity, and reasonable redox potential. Although four phases of Nb2O5 including hexagonal, orthorhombic, tetragonal, and monoclinic polymorphs show diverse characteristics in electrochemical performance, stable lifetime, high specific capacity, and fast intercalation properties cannot be delivered simultaneously with a single phase. Herein, this issue is addressed by generating a homogeneous mixture of orthorhombic and monoclinic crystals at the nanoscale. Reversible lithium-ion intercalation/deintercalation of the monoclinic phase is achieved, and exceptional lithium storage sites are created at the interface of the two phases. As a result, electrochemical features of stable lifetime from the orthorhombic phase and high specific performance from the monoclinic phase are harmoniously combined. This dual-phase Nb2O5/C nanohybrids deliver as high as 380 mA h g-1 (0.01-3.0 V) and 184 mA h g-1 (1.0-3.0 V) after 200 cycles. The essential principle of property enhancement is further confirmed through in situ XRD measurements and DFT calculations. The dual-phase concept can be further applied on electrodes with multiphases to achieve high electrochemical performance.
Keywords: Nb2O5 nanohybrids; coupling of electrochemical performances; dual phase; lithium-ion battery anode; structure design.