Water scarcity and water pollution have become increasingly severe, and therefore, the purification of water resources has recently garnered increasing attention. Given its position as a major water resource, the efficient purification of drinking water is of crucial importance. In this study, we adopted a phase transition method to prepare ZrO2/BCM (bamboo cellulose membranes), after which we developed IP-ZrO2/BC-NFM (bamboo cellulose nanofiltration membranes) through interfacial polymerization using piperazine (PIP) and tricarbonyl chloride (TMC). Subsequently, we integrated these two membranes to create a combined "ultrafiltration + nanofiltration" membrane process for the treatment of drinking water. The membrane combination process was conducted at 25 °C, with ultrafiltration at 0.1 MPa and nanofiltration at 0.5 MPa. This membrane combination, featuring "ultrafiltration + nanofiltration," had a significant impact on reducing turbidity, consistently maintaining the post-filtration turbidity of drinking water at or below 0.1 NTU. Furthermore, the removal rates for CODMN and ammonia nitrogen reached 75% and 88.6%, respectively, aligning with the standards for high-quality drinking water. In a continuous 3 h experiment, the nanofiltration unit exhibited consistent retention rates for Na2SO4 and bovine serum protein (BSA), with variations of less than 5%, indicating exceptional separation performance. After 9 h of operation, the water flux of the nanofiltration unit began to stabilize, with a decrease rate of approximately 25%, demonstrating that the "ultrafiltration + nanofiltration" membrane combination can maintain consistent performance during extended use. In conclusion, the "ultrafiltration + nanofiltration" membrane combination exhibited remarkable performance in the treatment of drinking water, offering a viable solution to address issues related to water scarcity and water pollution.
Keywords: ZrO2; cellulose; drinking water; nanofiltration membrane; separation performance; ultrafiltration membrane.