The work is aimed at the development of an energy-saving technique involving the partial carboxylation of powdered lignocellulose products from the straw of annual agricultural plants and the use of the obtained products in rubber compositions as a water-swelling filler. Lignocellulose powder from oat straw (composition: α-cellulose-77.0%, lignin-3.8%, resins and fats-1.8%) was used for carboxylation without preliminary separation into components. Microwave radiation was used to activate the carboxylation process. This reduced the reaction time by 2-3 times. The synthesized products were analyzed by IR spectroscopy, thermogravimetry and scanning electron microscopy. Industrial product sodium carboxymethylcellulose (Na-CMC) was used as a swelling filler for comparison. The swelling fillers were fractionated by the sieve method; particles with the size of 0-1 mm were used for filling rubber compounds. The amount of swelling filler was 150 parts per 100 parts of rubber (phr). Due to the high filling of rubber compounds, plasticizer Oxal T-92 was added to the composition of a number of samples to facilitate the processing and uniform distribution of ingredients. The rubber composition was prepared in two stages. In the first stage, ingredients without swelling filler were mixed with rubber on a laboratory two-roll mill to create a base rubber compound (BRC). In the second stage, the BRC was mixed with the swelling filler in a closed laboratory plasti-corder rubber mixer, the Brabender Plasti-Corder® Lab-Station. Vulcanization was carried out at 160 °C. For the obtained samples, the physical-mechanical and sorption properties were determined. It has been shown that the carboxylated powdered lignocellulose from oat straw increases the strength properties of rubber in comparison with Na-CMC. It has been shown that when the carboxylated powdered lignocellulose from oat straw is introduced into the rubber composition, the degree of rubber swelling in aqueous solutions of various mineralizations increases by 50 and 100% in comparison with a noncarboxylated lignocellulose.
Keywords: IR spectrum; carboxylation; flotoreagent oxal; microwave radiation; nitrile butadiene rubber; powdered lignocellulose; swelling rubber.