Utilizing waste materials in producing ultra-high-performance concrete (UHPC) represents a highly effective approach to creating environmentally sustainable concrete using renewable resources. This study focused on incorporating ground glass cullet (GP) at various replacement levels in UHPC production. Additionally, plastic bottle fibers (PBFs) were derived from discarded plastic bottles and employed in the mix. The replacement levels for GP spanned from 0% to 40%. Single-use plastic bottles were transformed into strip fibers, both with and without the inclusion of microsteel fibers, at varying contents of 1.1% and 2.2% (volume-based). A single-fiber test was conducted on PBFs under different strain rates. The introduction of optimal GP content had a profound positive iMPact on compressive strength. Incorporating 2.2% plastic strips induced strain hardening behavior, while further inclusion of microsteel fibers resulted in substantial enhancements in mechanical properties. Two types of microsteel fibers were employed, characterized by different aspect ratios of 65 and 100. The optimum GP content was identified as 10%. Moreover, the UHPC mix achieved superior compressive strength, exceeding 140 MPa when composed of 1.3% (volume-based) microsteel fibers with an aspect ratio of 65 and 2.2% PBF (volume-based). Notably, mixtures featuring microsteel fibers with a higher aspect ratio demonstrated the highest flexural strength, exceeding 8000 N in the presence of 2.2% PBF. Longer microsteel fibers exhibited adequate slip properties, facilitating strain transfer and achieving a strain-hardening response in conjunction with plastic bottle fibers. These findings illuminate the potential for harnessing hazardous waste materials to improve the performance and sustainability of UHPC formulations.
Keywords: glass cullet; mechanical strength; plastic bottle fibers; recycling hazardous waste materials; slump–flow; ultra-high-performance concrete (UHPC).