A large amount of open-dumped electrolytic manganese residue (EMR) has posed a severe threat to the ecosystem and public health due to the leaching of ammonia (NH4+) and manganese (Mn). In this study, CaO addition coupled with low-temperature roasting was applied for the treatment of EMR. The effects of roasting temperature, roasting time, CaO-EMR mass ratio and solid-liquid ratio were investigated. The most cost-effective and practically viable condition was explored through response surface methodology. At a CaO: EMR ratio of 1:16.7, after roasting at 187 °C for 60 min, the leaching concentrations of NH4+ and Mn dropped to 10.18 mg/L and 1.05 mg/L, respectively, below their discharge standards. In addition, the magnesium hazard (MH) of EMR, which was often neglected, was studied. After treatment, the MH of the EMR leachate was reduced from 60 to 37. Mechanism analysis reveals that roasting can promote NH4+ to escape as NH3 and convert dihydrate gypsum to hemihydrate gypsum. Mn2+ and Mg2+ were mainly solidified as MnO2 and Mg(OH)2, respectively. This study proposes an efficient and low-cost approach for the treatment of EMR and provides valuable information for its practical application.
Keywords: CaO; Electrolytic manganese residue (EMR); Low-temperature roasting; Magnesium hazard (MH); Mn immobilization; NH4 + removal.
© 2024. The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature.