In this work, we investigated the MOCVD conditions to synthesize thin films with the hexagonal P63cm h-LuMnO3 phase as a potential low-band gap ferroelectric material. The main parameters investigated were the ratio of organometallic starting materials, substrate temperature, and annealing effect. Two different substrates were used in the study: fused silica (SiO2) glass and platinized silicon (Pt\Ti\SiO2\Si(100)). In order to investigate the thermodynamic stability and quality of the developed phases, a detailed analysis of the crystal structure, microstructure, morphology, and roughness of the films was performed by X-ray diffractometer, scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), Raman spectroscopy, and piezoelectric force microscopy (PFM). Molar compositions in the film within 0.93 < |Lu|/|Mn| < 1.33 were found to be suitable for obtaining a single-phase h-LuMnO3. The best films were obtained by depositions at 700 °C, followed by thermal treatments at 800 °C for long periods of up to 12 h. These films exhibited a highly crystalline hexagonal single phase with a relatively narrow direct band gap, around 1.5 eV, which is within the expected values for the h-LuMnO3 system.
Keywords: MOCVD; narrow band gap; oxides; photo-ferroelectrics; thin films.