Oxide-dispersion- and hard-particle-strengthened (ODS) laser-cladded single-layer multi-tracks with a Ni-based alloy composition with 20 wt.% μm-WC particles and 1.2 wt.% nano-Y2O3 addition were produced on ultra-high-strength steel in this study. The investigation of the composite coating designed in this study focused on the reciprocating friction and wear workpiece surface under heavy load conditions. The coating specimens were divided into four groups: (i) Ni-based alloy, nano-Y2O3, and 2 μm-WC (2 μm WC-Y/Ni); (ii) Ni-based alloy with added 2 μm-WC (2 μmWC/Ni); (iii) Ni-based alloy with added 80 μm-WC (80 μmWC/Ni); and (iv) base metal ultra-high-strength alloy steel 30CrMnSiNi2A. Four conclusions were reached: (1) Nano-Y2O3 could effectively inhibit the dissolution of 2 μm-WC. (2) It can be seen from the semi-space dimensionless simulation results that the von Mises stress distribution of the metal laser composite coating prepared with a 2 μm-WC particle additive was very uniform and it had better resistance to normal impact and tangential loads than the laser coating prepared with the 80 μm-WC particle additive. (3) The inherent WC initial crack and dense stress concentration in the 80 μm-WC laser coating could easily cause dislocations to accumulate, as shown both quantitatively and qualitatively, resulting in the formation of micro-crack nucleation. After the end of the running-in phase, the COF of the 2 μm-WC-Y2O3/Ni component samples stabilized at the minimum of the COF of the four samples. The numerical order of the four COF curves was stable from small to large as follows: 2 μm-WC-Y2O3/Ni, 2 μm-WC/Ni, 80 μm-WC/Ni, and 30CrMnSiNi2A. (4) The frictional volume loss rate of 2 μm-WC-Y2O3/Ni was 1.3, which was significantly lower than the corresponding values of the other three components: 2.4, 3.5, and 13.
Keywords: Ni-based alloy coating; ODS; dispersion strengthen; nano-Y2O3; μm-WC.