The hybridization of inorganic and organic components is a promising strategy to build functional materials. Among several functions, luminescence is an important function which should be considered for practical usage. Inorganic-organic hybrid luminescent materials have been investigated as phosphors, sensors, and lasers. Organic luminescent centers such as dye molecules have often been hybridized with inorganic matrices. Polyoxometalate anions (POMs) are effective inorganic luminescent centers due to their luminescent properties and structural designability. However, most luminescent POM components are limited to lanthanide-based POMs. In this report, a photoluminescent inorganic-organic hybrid crystal based on a non-lanthanide POM was successfully synthesized as a single crystal. Anderson-type hexamolybdochromate ([CrMo6O18(OH)6]3-, CrMo6) anion exhibiting emission derived from Cr3+ was utilized with n-dodecylammonium ([C12H25NH3]+, C12NH3) surfactant cation to obtain a photoluminescent hybrid crystal. The grown single crystal of C12NH3-CrMo6 comprised a distinct layered structure consisting of inorganic CrMo6 layers and interdigitated C12NH3 layers. In the CrMo6 layers, the CrMo6 anions were associated with water molecules by hydrogen bonding to form a densely packed two-dimensional network. Steady-state and time-resolved photoluminescence spectroscopy revealed that the C12NH3-CrMo6 hybrid crystal exhibited characteristic emission from the CrMo6 anion. Preliminary lasing properties were also observed for C12NH3-CrMo6, which shows the possibility of using the C12NH3-CrMo6 hybrid crystal as an inorganic-organic hybrid laser.
Keywords: inorganic–organic; photoluminescence; polyoxometalate; single crystal; surfactant.