The effect of laser irradiation and tensile stress on the microstructure and soft magnetic properties of the FeSiBNbCu nanocrystalline alloy prepared using a continuous laser has been investigated. The experimental results indicate that a decreased laser scanning speed provides more thermal energy to induce nanocrystals and encourage grain growth. When the scanning speed is excessively high, the crystallization process will cease due to a lack of energy to drive diffusion phase transitions. Nevertheless, the introduction of tensile stress could significantly promote crystallization in FeSiBNbCu alloy samples irradiated at these high laser scanning speeds. This phenomenon can be attributed to the augmentation of compressive thermal stress at the interface between the laser-treated track and the untreated region. This heightened compressive stress promotes the diffusivity of atoms, and, as a result, the transformation from amorphous to crystalline states can be enhanced. As the applied tensile stress increases, both grain size and crystalline volume fraction exhibit a proportional augmentation. Consequently, these changes manifest in the soft magnetic properties. The crystalline volume fraction can reach 62%, and the coercivity is 2.9 A/m at the optimized scanning speed; these values correspond to 54% and 3.3 A/m under specific tensile stress loading.
Keywords: Fe-based nanocrystalline; laser irradiation; soft magnetic properties; tensile stress.