The reversible and durable operation of sodium metal batteries at low temperatures (LT) is essential for cold-climate applications but is plagued by dendritic Na plating and unstable solid-electrolyte interphase (SEI). Current Coulombic efficiencies of sodium plating/stripping at LT fall far below 99.9%, representing a significant performance gap yet to be filled. Here, the solvation structure of the conventional 1 m NaPF6 in diglyme electrolyte by facile cyclic ether (1,3-dioxolane, DOL) dilution is efficiently reconfigured. DOL diluents help shield the Na+-PF6 - Coulombic interaction and intermolecular forces of diglyme, leading to anomalously high Na+-ion conductivity. Besides, DOL participates in the solvation sheath and weakens the chelation of Na+ by diglyme for facilitated desolvation. More importantly, it promotes concentrated electron cloud distribution around PF6 - in the solvates and promotes their preferential decomposition. A desired inorganic-rich SEI is generated with compositional uniformity, high ionic conductivity, and high Young's modulus. Consequently, a record-high Coulombic efficiency over 99.9% is achieved at an ultralow temperature of -55 °C, and a 1 Ah capacity pouch cell of initial anode-free sodium metal battery retains 95% of the first discharge capacity over 100 cycles at -25 °C. This study thus provides new insights for formulating electrolytes toward increased Na reversibility at LT.
Keywords: Na plating/stripping reversibility; diluent; electrolyte solvation; low temperature; sodium metal battery.
© 2024 Wiley‐VCH GmbH.