Augmented physical, mechanical, and cellular responsiveness of gelatin-aldehyde modified xanthan hydrogel through incorporation of silicon nanoparticles for bone tissue engineering

Abstract

Bioactive scaffolds fabricated from a combination of organic and inorganic biomaterials are a promising approach for addressing defects in bone tissue engineering. In the present study, a self-crosslinked nanocomposite hydrogel, composed of gelatin/aldehyde-modified xanthan (Gel-AXG) is successfully developed by varying concentrations of porous silicon nanoparticles (PSiNPs). The effect of PSiNPs incorporation on physical, mechanical, and biological performance of the nanocomposite hydrogel is evaluated. Morphological analysis reveals formation of highly porous 3D microstructures with interconnected pores in all nanocomposite hydrogels. Increased content of PSiNPs results in a lower swelling ratio, reduced porosity and pore size, which in turn impeded media penetration and slowed down the degradation process. In addition, remarkable enhancements in dynamic mechanical properties are observed in Gel-AXG-8%Si (compressive strength: 0.6223 MPa at 90 % strain and compressive modulus: 0.054 MPa), along with improved biomineralization ability via hydroxyapatite formation after immersion in simulated body fluid (SBF). This optimized nanocomposite hydrogel provides a sustained release of Si ions at safe dose levels. Furthermore, in-vitro cytocompatibility studies using MG-63 cells exhibited remarkable performance in terms of cell attachment, proliferation, and ALP activity for Gel-AXG-8%Si. These findings suggest that the prepared nanocomposite hydrogel holds promising potential as a scaffold for bone tissue engineering.

Keywords: Aldehyde-modified xanthan gum; Bone tissue engineering; Gelatin; Nanocomposite hydrogel; Porous silicon nanoparticles.