Strain built-in electronic and optoelectronic devices can influence their properties and lifetime. This effect is particularly significant at the interface between two-dimensional materials and substrates. One such material is epitaxial hexagonal boron nitride (h-BN), which is grown at temperatures often exceeding 1000 °C. Due to the high growth temperature, h-BN based devices operating at room temperature can be strongly affected by strain generated during cooling due to the differences in lattice thermal expansion of h-BN and the substrate. Here, we present results of temperature-dependent Raman studies of the in-plane E2ghighphonon mode in the temperature range of 300-1100 K measured for h-BN grown by metalorganic vapor phase epitaxy. We observe a change, by an order of magnitude, in the rate of the temperature-induced frequency shift for temperatures below 900 K, indicating a strong reduction of the effective h-BN/substrate interaction. We attribute this behavior to the creation of h-BN wrinkles which results in strain relaxation. This interpretation is supported by the observation that no change of layer/substrate interaction and no wrinkles are observed for delaminated h-BN films transferred onto silicon. Our findings demonstrate that wrinkle formation is an inherent process for two-dimensional materials on foreign substrates that has to be understood to allow for the successful engineering of devices based on epitaxially grown van der Waals heterostructures.
Keywords: Raman spectroscopy; hexagonal boron nitride; metalorganic vapor phase epitaxy; strain; thermal expansion; wrinkles.
Creative Commons Attribution license.