In this study, the efficiency of mechanically alloyed Fe80Si10B10 in degrading basic red 46 azo dye is investigated. Moreover, the influences of different parameters, such as pH and time, on the elimination of the aromatic derivatives obtained as by-products of the fracture of the azo group are also analyzed. After beginning the reduction to the normal conditions of pH (4.6) and temperature, the experimental findings showed a discoloration of 97.87% after 20 min. The structure and morphology of the nanocrystalline Fe80Si10B10 powder were characterized by SEM and XRD before and after use in the degradation process. The XRD patterns of the Fe-Si-B powder after redox reaction suggest that the valent zero Fe of the alloy is the reducing agent. Powdered cork was then used as a biosorbent for the removal of the by-products generated, resulting in increasing removal percentages from pH 7 (26%) to pH 9 (62%) and a contact time of 120 min. The FTIR spectrum of the cork after adsorption shows a shift of the bands, confirming the interaction with the aromatic amines. The present findings show that metallic powders and natural cork perform well together in removing azo dye solutions and their degradation products.
Keywords: adsorption; azo dye; cork; redox process; wastewater.