Polyvinyl chloride (PVC) waste plastic is a typical solid waste. In this paper, the dechlorination and carbonization behavior of PVC in ethanol-water/water system under different process parameters (temperature, residence time, solid-liquid ratio) was studied, and hydrothermal carbon was characterized by SEM, elemental analysis, TG-DTG, XPS, Py-GC/MS. The results show that temperature is the key to the hydrothermal dechlorination of PVC, and the dechlorination efficiency of PVC is the highest by parameter optimization (220°C-90 min-10% S/D-80% E/D), which can reach 96.33 %. With the removal of Cl, the surface of the PVC matrix changed from full and smooth flocculent to honeycomb with uniform pore size distribution. Thermogravimetric analysis shows that the combustion of hydrochar can be divided into three stages: HCl precipitation and volatile combustion, semi-coke and coke combustion, and fixed carbon combustion. The combustion parameters and kinetic parameters of hydrochar were measured, and it was found that the hydrothermal carbonization of PVC at higher temperatures and ethanol-water ratio could improve the combustion performance of hydrochar. The highest calorific value can reach 36.68 MJ/mol. Py-GC/MS analyzed the distribution of the pyrolysis products, and alkylbenzene and aliphatic were the main products of pyrolysis. The structural analysis of hydrochar showed that C-C and CC accounted for the largest proportion, accompanied by a small amount of C-O and CO and trace C-Cl. The possible reaction mechanism of the hydrothermal carbonization of PVC was analyzed based on the distribution of functional groups and compound composition. This work provides an effective and sustainable method for the recycling of refractory chlorinated plastics.
Keywords: Combustion behavior; Dechlorination; Hydrothermal carbonization; Path analysis; Polyvinyl chloride.
Copyright © 2023 Elsevier Inc. All rights reserved.