Eco-friendly mixed metal (Mg-Ni) ferrite nanosheets for efficient electrocatalytic water splitting

Nyemaga M Malima; Malik Dilshad Khan; Siphamandla C Masikane; Felipe M de Souza; Jonghyun Choi; Ram K Gupta; Neerish Revaprasadu

doi:10.1038/s41598-023-49259-y

Eco-friendly mixed metal (Mg-Ni) ferrite nanosheets for efficient electrocatalytic water splitting

Sci Rep. 2023 Dec 13;13(1):22179. doi: 10.1038/s41598-023-49259-y.

Authors

Nyemaga M Malima^{1

2}, Malik Dilshad Khan³, Siphamandla C Masikane¹, Felipe M de Souza⁴, Jonghyun Choi⁴, Ram K Gupta⁴, Neerish Revaprasadu⁵

Affiliations

¹ Department of Chemistry, University of Zululand, Private Bag X1001, KwaDlangezwa, 3880, South Africa.
² Department of Chemistry, College of Natural and Mathematical Sciences, University of Dodoma, P.O. Box 338, Dodoma, Tanzania.
³ Department of Chemistry, University of Zululand, Private Bag X1001, KwaDlangezwa, 3880, South Africa. malikdilshad@hotmail.com.
⁴ Department of Chemistry, National Institute for Materials Advancement, Pittsburg State University, Pittsburg, KS, 66762, USA.
⁵ Department of Chemistry, University of Zululand, Private Bag X1001, KwaDlangezwa, 3880, South Africa. RevaprasaduN@unizulu.ac.za.

Abstract

Eco-friendly and cost-effective catalysts with multiple active sites, large surface area, high stability and catalytic activity are highly desired for efficient water splitting as a sustainable green energy source. Within this line, a facile synthetic approach based on solventless thermolysis was employed for the simple and tunable synthesis of Ni_1-xMg_xFe₂O₄ (0 ≤ x ≤ 1) nanosheets. The characterization of nanosheets (via p-XRD, EDX, SEM, TEM, HRTEM, and SAED) revealed that the pristine ferrites (NiFe₂O₄ and MgFe₂O₄), and their solid solutions maintain the same cubic symmetry throughout the composition regulation. Elucidation of the electrochemical performance of the nanoferrite solid solutions showed that by tuning the local chemical environment of Ni in NiFe₂O₄ via Mg substitution, the intrinsic catalytic activity was enhanced. Evidently, the optimized Ni_0.4Mg_0.6Fe₂O₄ catalyst showed drastically enhanced HER activity with a much lower overpotential of 121 mV compared to the pristine NiFe₂O₄ catalyst. Moreover, Ni_0.2Mg_0.8Fe₂O₄ catalyst exhibited the best OER performance with a low overpotential of 284 mV at 10 mA/cm² in 1 M KOH. This enhanced electrocatalytic activity could be due to improved electronic conductivity caused by the partial substitution of Ni²⁺ by Mg²⁺ in the NiFe₂O₄ matrix as well as the synergistic effect in the Mg-substituted NiFe₂O₄. Our results suggest a feasible route for developing earth-abundant metal oxide-based electrocatalysts for future water electrolysis applications.