In the field of electromagnetic wave (EMW) absorption, carbon matrix materials based on metal-organic frameworks (MOFs) have drawn more interest as a result of their outstanding advantages, such as porous structure, lightweight, controlled morphology, etc. However, how to broaden the effective absorption bandwidth [EAB; reflection loss (RL) ≤ -10 dB] is still a challenge. In this paper, large microsphere structures of a Co/C composite composed of small particle clusters were successfully prepared by the solvothermal method and annealing treatment. At a filling ratio of 40 wt %, the Co/C composite shows attractive microwave absorption (MA) performance after being annealed at 600 °C in an atmosphere of argon. With an EAB of 6.32 GHz (9.92-16.24 GHz) and a thickness of just 2.57 mm, the minimum RL can be attained at -54.55 dB. Most importantly, the EAB can attain 7.12 GHz (10.88-18.0 GHz) when the thickness is 2.38 mm, which is larger than that of the majority of MOF-derived composites. The superior MA performance is strongly related to excellent impedance matching and a higher attenuation constant. This study provides a simple strategy for synthesizing a MOF-derived Co/C composite with a wide EAB.
Keywords: Co/C composite; electromagnetic wave absorption; metal−organic frameworks (MOFs); microsphere; wide effective absorption bandwidth.