In Vitro Evaluation of Candida albicans Adhesion and Related Surface Properties of CAD/CAM Denture Base Resins

Shaimaa M Fouda; Mohammed M Gad; Reem Abualsaud; Passent Ellakany; Hamad S AlRumaih; Faraz A Farooqi; Asif Matin; Doaa M Al-Eraky; Faisal D Al-Qarni; Fahad A Al-Harbi

doi:10.1055/s-0043-1774319

In Vitro Evaluation of Candida albicans Adhesion and Related Surface Properties of CAD/CAM Denture Base Resins

Eur J Dent. 2023 Dec 12. doi: 10.1055/s-0043-1774319. Online ahead of print.

Affiliations

¹ Department of Substitutive Dental Sciences, College of Dentistry, Imam Abdulrahman Bin Faisal University, Dammam, Saudi Arabia.
² Department of Dental Education, College of Dentistry, Imam Abdulrahman Bin Faisal University, Dammam, Saudi Arabia.
³ IRC Membranes and Water Security, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia.
⁴ Department of Biomedical Sciences, College of Medicine, Gulf Medical University, Ajman, United Arab Emirates.

PMID: 38086425
DOI: 10.1055/s-0043-1774319

Abstract

Objective: The aim of this study was to evaluate the surface roughness, contact angle, and adhesion of Candida albicans to computer-aided designing/computer-aided manufacturing (CAD/CAM) and heat-polymerized (HP) denture base materials.

Materials and methods: Specimens were allocated to six groups based on the composition of studied denture base materials, HP acrylic resin, milled resins (AvaDent and IvoCad), and 3D-printed resins (ASIGA, FormLabs, and NextDent). Ten specimens per group were used for each test (n = 10/test). Surface roughness and contact angles were analyzed using profilometer and goniometer, respectively. Adhesion of C. albicans was counted using colony-forming unit (CFU/mL). Means and standard deviations were calculated, and then one-way analysis of variance (ANOVA), followed by Tukey's post hoc test. Correlation of Candida adhesion and surface parameters was determined by using Pearson's correlation analysis.

Results: No statistically significant difference was noted in surface roughness between HP, milled, and 3D-printed denture base resins except NextDent, which showed significantly higher roughness in comparison to all other resins (p = 0.001). In terms of contact angle, milled resins had the lowest value, followed by HP, ASIGA, and FormLabs, whereas NextDent showed the highest contact angle (p = 0.001). C. albicans adhesion showed no significant difference between all denture base resins. A positive and significant correlation was found between C. albicans adhesion and contact angle (p = 0.003), while no correlation was reported between C. albicans adhesion and surface roughness (p = 0.523).

Conclusion: Adhesion of C. albicans was similar in all tested specimens. Surface roughness showed no significant difference between all groups except NextDent, which had the highest value. Milled denture base resins had the lowest contact angle among all groups.