In this work, solid-state reaction sintering was used to fabricate Ca7ZrAl6O18-Ca3Al2O6-CaZrO3:Eu3+ ternary composite ceramics and cements. The structural, microstructural, and spectroscopic properties of the ceramics with different Eu2O3 content were characterized by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS), and spectrofluorimetry, respectively. The XRD patterns analyzed with Rietveld refinement confirm the presence of the orthorhombic phase of Ca7ZrAl6O18 and the cubic phase of Ca3Al2O6 in all the samples, indicating that doping of Eu3+ slightly changes the crystalline structure of both aluminate phosphors. EDS analysis revealed that the Eu doping element was strongly concentrated to the two phases, i.e., Ca7ZrAl6O18 and Ca3Al2O6, with the Eu concentrations of 8.45 wt.% and 8.26 wt.%, respectively. The luminescent properties of the ceramics doped with different Eu3+ ion concentrations were investigated by excitation and emission spectroscopy at room temperature. These results were compiled using a laser with an optical parametric oscillator (OPO) system. The obtained spectra indicated changes in the luminescence intensity and shape occurring with phase composition and Eu2O3 concentration. The emission spectra of the ceramics exhibit a strong dependence on the excitation wavelength in the range from 210 to 300 nm, and invariably, five peaks were assigned to the 5D0 → 7FJ (J = 0, 1, 2, 3, 4) transitions of Eu3+. The luminescence spectroscopy was then used to trace the early and long-term hydration behavior of cements. Thus, luminescence spectroscopy may provide a new tool for non-destructive testing of cement-based structures.
Keywords: Ca7ZrAl6O18:Eu ceramics; structural and microstructural properties; tracing the early and long-term hydration.