This study aimed to formulate and characterize the experimental lollipops containing chitosan- zinc oxide nanoparticles (CH-ZnO NPs) and investigate their antimicrobial effects against some cariogenic bacteria. The CH-ZnO NPs were synthesized and characterized by X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR) analysis, and Transmission electron microscope (TEM). Then, four groups were made, including lollipops coated with 2 and 4 ml of CH-ZnO NPs, 0.7 ml CH-ZnO NPs incorporated lollipops, and those with no CH-ZnO NPs. Their antibacterial effectiveness against Streptococcus mutans and Lactobacillus acidophilus was evaluated by direct contact test and tissue culture plate method in planktonic and biofilm phases, respectively. Chlorhexidine mouthrinse (CHX) was used as a positive control group. In the planktonic phase, the antibacterial properties of both groups coated with CH-ZnO NPs were comparable and significantly higher than incorporated ones. There was no significant difference between CHX and the lollipops coated with 4 ml of NPs against S. mutans and CHX and two coated groups against L. acidophilus. None of the experimental lollipops in the biofilm phase could reduce both bacteria counts. The experimental lollipops coated with 2 and 4 ml of CH-ZnO NPs could reveal favorable antimicrobial properties against two cariogenic bacteria in the planktonic phase.
Keywords: Anti-caries lollipop; Chlorhexidine; Dental caries; Lactobacillus acidophilus; Nano chitosan; Streptococcus mutans; Zinc oxide.
© 2023. The Author(s).