Bagasse-derived biochar (SCB750) was prepared at 750 °C using Chinese sugarcane bagasse as a carbon source and then modified with KOH for the removal of the antibiotic norfloxacin (NOR) from aqueous solutions. 3K-SCB750, prepared using a solid-to-liquid mass ratio of bagasse:KOH = 1:3, was found to have the best adsorption performance for NOR. Under the conditions of pH 5, 25 °C, 2.4 g L-1 adsorbent, and 300 mg L-1 NOR, its adsorption of NOR reached equilibrium (97.5% removal) after 60 min. The adsorption behaviours were in line with the quasi-second-order kinetic and Langmuir isotherm models, respectively. The maximum theoretical adsorption capacity reached up to 157.4 mg·g-1 at 40 °C. The thermodynamic parameters showed that the adsorption of NOR onto 3K-SCB750 was a spontaneous, endothermic, and physical process. In addition, Brunauer-Emmett-Teller analysis (BET), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and Raman spectroscopy were conducted to investigate the structural and adsorption properties of 3K-SCB750. Fourier transform infrared spectroscopy (FTIR) was also applied to understand the mechanism of adsorption of NOR onto 3K-SCB750. All of the results indicated that 3K-SCB750 had a large specific surface area of 1038.8 m2·g-1, an average pore size of 1.9 nm, and hierarchical structures with random pores and cracks for efficient removal of NOR. NOR adsorption mechanisms on 3K-SCB750 were related to the pore-filling effect and electrostatic attraction. Therefore, 3K-SCB750 biochar may be used as a promising adsorbent of antibiotics in wastewaters.
Keywords: Chinese sugarcane bagasse; KOH activated; adsorption; biochar; norfloxacin removal.