This paper aimed to evaluate the biological damages towards diseased cells caused by the use of MgO nanoparticles (NPs). The NPs are produced by a calcination process of a precursor, which is an aqueous suspension of nanostructured Mg(OH)2, in turn synthesized following our original, time-energy saving and scalable method able to guarantee short times, high yield of production (up to almost 10 kg/week of NPs), low environmental impact and low energy demand. The MgO NPs, in the form of dry powders, are organized as a network of intercrystallite channels, in turn constituted by monodispersed and roughly spherical NPs < 10 nm, preserving the original pseudo hexagonal-platelet morphology of the precursor. The produced MgO powders are diluted in a PBS solution to obtain different MgO suspension concentrations that are subsequently put in contact, for 3 days, with melanoma and healthy cells. The viable count, made at 24, 48 and 72 h from the beginning of the test, reveals a good cytotoxic activity of the NPs, already at low MgO concentrations. This is particularly marked after 72 h, showing a clear reduction in cellular proliferation in a MgO-concentration-dependent manner. Finally, the results obtained on human skin fibroblasts revealed that the use MgO NPs did not alter at all both the vitality and proliferation of healthy cells.
Keywords: HRTEM; MgO against cancer growth; MgO nanoparticles; XRD; growth curves of melanoma cells; ion exchange process; scalable and time-energy synthesis; therapeutic applications.