The ultrasonic-assisted spray dryer, also known as a nano spray dryer and predominantly used on a lab scale in the pharmaceutical and food industries, enables the production of nanometer-sized particles. In this study, the nano spray dryer was applied to cellulosic materials, such as cellulose nanofibrils (CNFs) and cellulose nanocrystals (CNCs). CNC suspensions were successfully dried, while the CNF suspensions could not be dried, attributable to their longer fibril lengths. The nano spray drying process was performed under different drying conditions, including nebulizer hole sizes, solid concentrations, and gas flow rates. It was confirmed that the individual particle size of nano spray-dried CNCs (nano SDCNCs) decreased as the nebulizer hole sizes and solid contents of the suspensions decreased. The production rate of the nano spray dryer increased with higher solid contents and lower gas flow rates. The resulting nano SDCNCs were added to a polyvinyl alcohol (PVA) matrix as a reinforcing material to evaluate their reinforcement behavior in a plastic matrix using solvent casting. After incorporating the 20 wt.% nano SDCNCs into the PVA matrix, the tensile strength and tensile modulus elasticity of the neat PVA nanocomposite film increased by 22% and 32%, respectively, while preserving the transparency of the films.
Keywords: cellulose nanocrystals; nano spray dryer; polyvinyl alcohol.